The Characteristics of Leaky Surface Acoustic Wave of Proton-Exchanged Lithium Tantalite

TUNG FANG Institutional Repository > 電子與資訊系(遊戲動畫系、動畫科) > 會議論文 > Item 987654321/374

請使用永久網址來引用或連結此文件: http://163.15.40.127/ir/handle/987654321/374

題名:	The Characteristics of Leaky Surface Acoustic Wave of Proton-Exchanged Lithium Tantalite
作者:	Chung, Chung-Jen Chen, Ying-Chung Wei, Ching-Liang 高國陞 Kao, Kuo-Sheng Cheng, Chien-Chuan (東方技術學院電子與資訊系)
貢獻者:	東方技術學院電子與資訊系
關鍵詞:	proton exhange;lithium tantalite;leaky surfaceacoustic wave;temperature coefficient of frequency
日期:	2004-08
上傳時間:	2009-11-27 09:47:29 (UTC+8)
摘要:	Proton exchange (PE) is an attractive method for the fabrication of optical and acoustic waveguides in lithium tantalite (LiTaO{sub}3) substrate. Octanoic acid was used for the fabrication of PE LiTaO{sub}3 waveguides. After the PE process, the resultant substrate showed a damage-free surface from observations by scanning electron microscopy (SEM). And X-ray diffraction (XRD) was adopted to identify the crystalline structure of LiTaO{sub}3. From the X-ray diffraction (XRD) results, the reflection peak of (306) was shifted after PE process. The influences of the exchanging time on properties of leaky surface acoustic wave (LSAW) devices were discussed. The single electrode geometry of interdigital transducers (IDTs) was adopted to excite and receive the acoustic wave. The wavelength (λ) of the LSAW is 32μm. The frequency response of the LSAW is measured using an HP 8720ET network analyzer. The velocity of LSAW was decreased as the increase of PE time; nevertheless, the range of variation was quite small. Measurements of the temperature dependence of LSAW velocity were carried in the temperature range from 0℃to 80℃. The temperature coefficient of frequency (TCP) of LSAW devices was significantly increased by the increase of PE time. The PE process changed the characteristics of material and specific property can be obtained.
關聯:	2004 IEEE Utrasonics Symposium Publication Date: 23-27 Aug. 2004 Volume: 2, On page(s): 1545- 1548 Vol.2